Glass sodium liquid 20 kg

STRUCTURE:

• Appearance: dense liquid yellow or gray (greenish shade) colors.
• Silicate module: from 2,8-3,2.
• Density, g/cm 3: from 1,4 - 1,47.

TU 200101299.005-2010

APPOINTMENT:

It is applied:

• In the textile industry as the bleaching means for fabrics and yarn.
• In soap-producing, fatty, chemical industry, as the making component.
• In the paper industry, including for production of a cardboard container, as binding material, for pasting of a cardboard and paper.
• In mechanical engineering industry, in ferrous metallurgy, for production of welding materials, at production of forms and cores in foundry production as binding material.
• At mineral processing as floatation reagent.
• In production of putty, glue, impregnation, as the making component.

Recommendations about application:

1. For filling of cracks and emptiness in walls partitions. Structure: liquid glass, cement, sand (in proportions 1:1:3). To prepare a batch of cement and sand, an amount of water no more than 25% (weight) of amount of liquid glass. To add this mix to liquid glass at continuous hashing.
2. For coupler surface primer: 12 kg of liquid glass + 12 kg of cement. To mix cement with water, an amount of water no more than 25% (weight) of amount of liquid glass. In the portions to add to liquid glass at continuous hashing.
3. For a waterproofing of wells. To apply liquid glass on well walls, to prepare solution (cement, liquid glass, the sifted small sand in a proportion 1:1:1 orders of preparation according to the item of l.) and to carry out repeated putty of a well.
4. For external works, a fireproof plastering, preparation of acidproof solutions. Structure: liquid glass, cement, sand in a proportion 1,5:1,5:4. To prepare a batch of cement and sand, an amount of water no more than 25% (weight) of amount of liquid glass. To add this mix to liquid glass at continuous hashing.
5. Preparation of the painting solutions with ochre, minium, a chrome oxide. Does not burn out in the sun, well washes.
6. For pro-dabs of wooden parts. To miss the mark walls, ceilings with liquid glass for creation of protection against dampness, a mold, a fungus.
7. For a covering of a floor garret and basements on purpose fire - and waterproofings.

WAY OF STORAGE:

To store in densely closed container at a temperature not lower than + 5 degrees.

Warranty period of storage of 12 months from the date of production.

PRECAUTIONARY MEASURES:

Liquid glass sodium pozharovzryvobezopasny.

At hit in eyes immediately to wash out water.

INCREASE IN WATER RESISTANCE OF THE PLASTERED AND CONCRETE SURFACES:

To cover the plastered or concrete surface 1 - 2 time of 10-15% with water solution of liquid sodium glass and then glass of a normal consistence. After drying a surface to cover 3 - 5% with water solution of chloride calcium, sulfate aluminum or weak limy solution.

PREPARATION OF WATERPROOF PLASTER:

To prepare plaster in the ratio:

One volume of cement and 2-3 volumes of sand. As solvent to use 10-15% water solution of liquid sodium glass.

Surface to plaster and level.

After plaster hardening to miss the mark a surface with liquid sodium glass of a normal consistence.