- BrandЛакокраска, ОАО
- Country of manufactureBelarus
- Basis of the enamelAlkyd
- Number of componentsTwo-component
- PurposeUniversal
- Degree of brillianceFrosted
- ColorIn assortment
Type: Enamel is a suspension of pigments and fillers in a solution of an alkyd and melamine - formaldehyde resins.
Scope: Enamel intended for protective and decorative metal coloring.
Specifications
| " | The name of indicators | requirements ROV |
| one | Color enamel coating | Must be within the tolerances established by the approval of the color samples correspond to a scale or color RAL register. |
| 2 | Appearance of the enamel coating | After drying the enamel must form a homogeneous semi - matt surface with a characteristic appearance resembling shagreen skin. |
| 3 | Viscosity according viscometer VZ - 246 (nozzle 4 mm) at a temperature (20,0 ± 0,5) ° C, not less than | 80 |
| 4 | Mass fraction of solids, %
black other colors |
54 - 60
61 - 69 |
| 5 | The degree of grinding of enamel, um, not more than | fifty |
| 6 | The drying time of up to 3 degrees at a temperature of (130 ± 2) ° C, min, max | 60 |
| 7 | Elasticity coating flexural mm, not more than | one |
| 8 | Impact resistance coating on the device U - 1, cm, at least | fifty |
| nine | coating gloss by photoelectric gloss meter SE - 2,% | 8 - 15 |
| 10 | Coating hardness pendulum device TML (pendulum A) rel. units. , at least | 0.26 |
| eleven | Spreading dried coating, g / m 2 , no more than | one hundred |
| 12 | Resistance to static action at (20 ± 2) ° C, h, min
distilled water gasoline industrial oil |
24 4 24 |
| thirteen | Life of the coating under operating conditions:
NF1, years, not less T1 years, at least |
2 one |
To eliminate condensation substrate temperature should be above the dew point temperature of not less than 3 ° C.
Advantages: Enamel provides a coating with a distinctive appearance resembling shagreen skin. Enamel coatings have high decorative properties when operating at atmospheric conditions and indoors. Coating enamels resistant to temperature changes in the range from minus 60 ° C to plus 60 ° C.
Recommendations on Application: Before applying the enamel primed surface sanded if necessary, dedusted, degreased and thoroughly dried. Previously painted surfaces purified by the fragile layers of the old coating, delaminated old coating removed, the entire surface is cleaned mechanically, dedusted, degreased and dried. To eliminate condensation substrate temperature should be above the dew point temperature of not less than 3 ° C. Recommended primers: PL - 03 R (for dyeing brass and steel) or primer GP - 0119, GP - 0119 "L", or PL - 03 F (for coloring of aluminum and its alloys). Previously painted surfaces must be cleaned of dust, grease, grind, degrease, dry and produce a test staining. In the case of blistering or peeling of the old coating should be removed.
Before applying the enamel thoroughly mixed, diluted with toluene in an amount of not more than 25% by weight of the undiluted enamel and then filtered through a mesh. The enamel is applied at a temperature below 5 ° C and a relative humidity of 80% . The enamel is applied by pneumatic spraying. The recommended coating system:
- first layer - priming PL - 03 K or GF - 0119, GP - 0119 "L", or PL - 03 J. Drying in accordance with the ROV active material.
- second layer - applying enamel ML - 158 by air pressure
0.3 - 0.4 MPa and extract at least 10 minutes at a temperature (20 ± 2) ° C.
- third layer - applying enamel ML - 158 by air pressure
0.05 MPa and drying for 60 minutes at a temperature of (130 ± 2) ° C.
The thickness of the dried coating complex - 55 - 80 microns. After staining should avoid strong mechanical stress for 7 days.
Flow enamel layer coating is 75 - 120 g / m², depending on the complexity of the surface to be painted, the color of enamel, staff, and other factors.
Coating Lifetime: The coating system consisting of two layers of enamel, applied to the primed surface (primer FL - 03 K according to GOST 9109 thickness of 10 - 15 microns) retains protective and decorative properties in conditions of moderately cold climate for at least 2 years and in a tropical climate within 1 year. The thickness of the dried complex coating is 55 - 80 microns.