Clay 88 - NP (TU 38.1051760 - 89) - a mixture of chloroprene rubber, rubber, neoprene, which is based phenol - formaldehyde resin. It is used for bonding cold rubber by rubber, cardboard, metal, glass, plastic surfaces, including rubber okrashennymi - bonding with each other.
Clay NP - 88 is used in:
- • Construction, installation of decorative coatings.
- • automotive industry, for sealing and mounting internal equipment and by - Delco.
- • Light (footwear) industry to connect components.
- • furniture industry for connecting and fastening the individual elements.
Adhesive 88 in the air does not produce toxic compounds, and also in the presence of various chemical substances, which allows its use in industry and in the home. 88 glue requires the preparation of the bonding surfaces, which are cleaned of dirt and dust.
If you find oily stains, residues of lubricants, they want to remove. The painted surface must be free of paint peeling. After cleaning the surfaces can begin to stick together. Advantages: Adhesive rubber 88 - NP has a greater resistance to degradation in the temperature range from 700 ° C to + - 500S in air and water (fresh and sea) srede - not aggressive to the bonding surfaces and does not promote corrosion in steel products and products from aluminum alloys .
|
number |
indicator |
The norm TU 38 105 540 - 85 |
|
1 |
Appearance |
Вязко - текучая масса от светло - желтого до светло - коричневого цвета(при температуре не ниже 150 С) |
|
2 |
Однородность |
Однороден |
|
3 |
Условная вязкость по вискозиметру ВЗ - 1(диаметр сопла 5,4 мм), с, в пределах |
15 - 40 |
|
4 |
Прочность связи резины П - 56,56(ТУ 380051166 - 98) со сталью Ст - 3 (ГОСТ 380 - 94) или алюминиевым сплавом Д - 16(ГОСТ 21488 - 97,ГОСТ21631 - 76) через 24ч после склеивания при температуре(23±5)0С: |
|
|
4.1 |
При отслаивании, Н/мм(кгс/см), не менее |
2,26(2,3) |
|
4.2 |
При отрыве, МПа (кгс/см2) не менее |
1,18(12,0) |
|
5 |
Скорость отслаивания резины П - 56 от алюминиевого сплава Д - 16 или стали Ст - 3 через (24±0,5) ч после склеивания клеем под воздействием отслаивающей нагрузки (0,31±0,05) Н/мм (0,32±0,06) кгс/см при температуре (70±2)0С, см/мин, не более |
0,6 |
Характеристики
| Страна производитель | Россия |